Top rated amorphous metal cores factory: We are a group company located in Foshan, China, with two manufacturing plants, coving a production area more than 70,000 Sqare meters. We specialized in a broadrange of tape wound cores in Amorphous metal materials, Nanocrystalline alloys, Silicon electrical steels, and Mu metal Nickel alloys, for a wide variety of applications including solar inverters, new energy vehicles, instrument transformers, current sensors, commonmode chokes, custom power transformers. We also manufacture high-performance components using our high-quality cores made in-house. The use of nanocrystalline core offers significant benefits such as increased efficiency, reduced size and weight of components, and enhanced reliability in power electronic systems. Discover a lot more information at nanocrystalline cores.

Characteristics and application of nanocrystalline magnetic core: High permeability, nanocrystalline Fe73 5Cu1Nb3Si13. 5B9 alloy has high saturation magnetic induction. The material becomes brittle after heat treatment and is easy to be processed into alloy powder. Compared with the nanocrystalline magnetic core wound with strip, the magnetic permeability of the nanocrystalline magnetic core is still very low and the soft magnetic properties are unstable. At present, the urgent problems to be solved are as follows: 1. Effectively control the growth of nanocrystals during heat treatment; 2. Molding of magnetic particle core; 3 Effect of heat treatment specification on soft magnetic properties of magnetic particle core.

However, at the same BM, the loss of Fe based amorphous alloy is smaller than that of 0.23mm thick 3% silicon steel. It is generally believed that the reason for low loss is the thin thickness and high resistivity of iron-based amorphous alloy strip. This is only one aspect. The main reason is that the iron-based amorphous alloy is amorphous, the atomic arrangement is random, there is no magnetocrystalline anisotropy caused by atomic directional arrangement, and there is no grain boundary causing local deformation and composition offset. Therefore, the energy barrier hindering domain wall motion and magnetic moment rotation is very small, with unprecedented soft magnetism, so it has high permeability, low coercivity and low loss.

Amorphous Core is preferred choice for transformers required low losses at high frequency. We have amorphous c-cores,amorphous ribbon cores,amorphous cut cores,amorphous core transformers . Please find out more about crgo core material. There are 50% and 80% nickel iron materials available, in which we manufactures Mumetal Toroidal core and Mumetal C-core, for the applications in high quality Current Transformers and power supplies industries.

As the iron core of the transformer, generally, 0.35mm thick cold rolled silicon steel sheet is selected. It is cut into long pieces according to the size of the required iron core, and then overlapped into “day” shape or “mouth” shape. In principle, in order to reduce eddy current, the thinner the silicon steel sheet, the narrower the spliced strip, and the better the effect. This not only reduces the eddy current loss and temperature rise, but also saves the material of silicon steel sheet. But in fact, when making silicon steel sheet iron core. Not only from the above favorable factors, because making the iron core in that way will greatly increase the working hours and reduce the effective section of the iron core. Therefore, when making transformer iron core with silicon steel sheet, we should start from the specific situation, weigh the advantages and disadvantages and choose the best size. Find extra details on transmartcore.com.

As the iron core of the transformer, generally 0.35mm thick cold-rolled silicon steel sheet is selected. It is cut into long pieces according to the size of the required iron core, and then overlapped into “day” shape or “mouth” shape. In principle, in order to reduce eddy current, the thinner the silicon steel sheet, the narrower the spliced strip, and the better the effect. This not only reduces the eddy current loss and temperature rise, but also saves the material of silicon steel sheet. But in fact, when making silicon steel sheet iron core. Not only from the above favorable factors, because making the iron core in that way will greatly increase the working hours and reduce the effective section of the iron core. Therefore, when making transformer iron core with silicon steel sheet, we should start from the specific situation, weigh the advantages and disadvantages and choose the best size.